Modern corrosion tests are becoming increasingly complex and multilayered.
The sequence of sophisticated temperature and humidity progressions up to frost storage attempts to simulate real environmental conditions in a comparable and time-lapsed manner.

For this purpose we offer test cabinets and chambers with a wide range of options.
For example, DIN 55635 (VDA 233-102) or similar tests are possible.

– Suitable for Corrosion tests according to ISO 6270-2, ISO 9227, ASTM B 177, VDA 621-415, PV 1208, PV 1209, PV 1210, ISO 11997, LV 124, Volvo 423-0014, Volvo STD 1027, SAE J 2334, DIN 55635, VDA 233-102, PPV 4017, Renault ECC 1, GMW 14872, GMW 3172 und more

DIN 55665 VDA233-102 Cyclic corrosion testing of materials and components in automotive construction

0 Preface

This specification has been created jointly by the automotive, steel and aluminum industry.

To document the close cooperation during the development of this agreed upon laboratoryscale cyclic corrosion test for the development of new materials and coatings for applications in the automotive industry, this specification is published with identical content as both StahlEisen-Prüfblatt 1850 and VDA-Recommendation 233-102.

1 Purpose and scope

The purpose of this specification is to provide

an accelerated test procedure for the assessment of the corrosion behaviour of components and of the corrosion protection provided by coating systems. The accelerated

test covers in particular the delamination/corrosion creep around a defined artificial

defect in a coating as well as surface and

edge corrosion on special test plates, bonding specimens or components. Compared to tests with a higher humidity availability a decreased ageing rate of adhesive is to be expected.

This laboratory-scale cyclic corrosion test is also suitable for assessing perforation corrosion in flanged areas or gaps and of unpainted surfaces.

This method induces corrosion processes and generates reproducible corrosion patterns which correlate well with the results obtained in natural weathering tests (DIN 55665) and driving operation. In particular, the corrosion patterns for the substrates steel, galvanised steel and aluminium closely reflect real-life phenomena. The test method is based on real corrosive climate conditions and delivers differentiated results for a large number of uses in automotive applications.

1.2. Disclaimer

The VDA recommendations are recommendations that are available for anyone to use. Anyone using these recommendations is responsible for ensuring that they are used correctly. The VDA recommendations give due consideration to the prevailing state-of-the-art at the time of publication. Use of the VDA recommendations does not allow a person to avoid assuming responsibility for his or her actions. In this respect, everyone acts at their own risk. The VDA and the parties involved in drawing up the VDA recommendations assume no liability whatsoever. We request that anyone encountering an error or the possibility of an incorrect interpretation when using the VDA recommendations contacts the VDA immediately so that any errors can be rectified.

The document is a translation of the German version. Therefore the German document represents the original and should be referenced in the case of discrepancies. Due to the fact that this document is a translation, it may be the case that the English text leaves room for interpretation because certain terms are often deeply rooted in the original language, and therefore it is not possible to translate them into another language without a certain degree of ambiguity arising.

2 Standards

DIN EN ISO 4628-8

Paints and varnishes - Evaluation of degradation of coatings – Designation of quantity and

size of defects, and of intensity of uniform changes in appearance -Part 8: Assessment of degree of delamination and corrosion around a scribe or other artificial defect

ISO 8573-1

Compressed air – Part 1: Contaminants and purity classes

DIN EN ISO 9227

Corrosion tests in artificial atmospheres – Salt spray tests

DIN EN 10130

Cold rolled low carbon steel flat products for cold forming

DIN 55665

Beschichtungsstoffe – Freibewitterung von Beschichtungen - Prüfung des Korrosionsschutzverhaltens

ISO 8407

Corrosion of metals and alloys – Removal of corrosions products from corrosion testspecimens

SEP 1160/Part 1

Evaluation of Weldable Corrosion Protection Primers for the Automotive Industry,

Part 1: Corrosion Performance

3 Equipment and consumables

- Programmable corrosion test chamber

- Temperature and relative humidity monitoring using a data logger

- Monitoring of constant testing conditions by means of mass-loss specimens

- Measuring cylinder plus funnel

- pH meter

4 Corrosion testing

The correct execution of VDA 233-102 requires a programmable test chamber allowing

continuous programming of temperature, relative humidity and salt spray.

The test should be carried out in a combination chamber allowing all programmed climates to be run, in order to ensure minimal disturbance of the climates. In exceptional cases, the test may also be conducted in several chambers.

All parts of the test equipment that come into contact with the salt spray atmosphere, condensate or test solutions shall be made of a material that is resistant to attack by the test

media and does not itself affect the action of the test solutions or the salt spray/condensate.

The test chamber design shall include equipment for cooling, heating, and pressure compensation, as well as the necessary instrumentation and control equipment to set and

maintain the climate data [temperature (DT=±2) °C, relative humidity (DRH=±3) %] in

the closed chamber at defined temperature/humidity points. A rate of temperature change of 1,5 K/min is recommended.

The test chamber geometry shall be designed such that no drops can fall from the ceiling or side walls onto the specimens positioned below them. After spraying, the test solutions may not be returned to the reservoir. The useable space for the test is defined as that part of the chamber which is outside the actual spray jet and within a constant distribution of the spray according to Section 4.3 as demonstrated.

4.1 Spray nozzle(s)

The nozzles used to generate the spray shall be suitable for the temperature range of the test and comply with the conditions set forth in Section 4.3. The flow-rate must be set and fixed so that it will be within the limits specified in Section 4.3. Care must be taken to ensure that the spray jet is not pointing directly at the specimens to be tested. The number and arrangement of the spray nozzles are to be selected such that the specifications for the useable space, according to Section

4.2 Test solution

The test shall be performed with a solution of one wt.% sodium chloride in water.

The sodium chloride is to be dissolved in distilled or deionised water with a maximum conductivity of 20 µS/cm at (25 ± 2) °C to ensure that a concentration of (10 ± 1) g/l is

achieved. The sodium chloride concentration of the sprayed and collected solution must

also be (10 ± 1) g/l. The relative density of such a (10 ± 1) g/l solution is 1.005 +/- 0.0005

g/cm3 at 25 °C. The quality of the deionised water, the salt and the pH-value of the collected solution are defined in DIN EN ISO 9227 (NSS-Test).

4.3 Flow rate and distribution of the spray The flow-rate of test solution according to Section 4.2 to be sprayed over a defined period of time shall be chosen, such that when the solution is sprayed into the empty corrosion testing chamber over a period of at least 3 h, the mean quantity of sprayed solution collected in each of the collecting recipients placed in the chamber is (3.0 ± 1.0) ml/h. Each of these recipients shall have a horizontal collecting area of approximately 80 cm2.

Suitable collecting recipients include glass or plastic funnels with a diameter of 100 mm

(equivalent to the above-mentioned collecting area) which are fitted via a plug to a measuring cylinder made of glass or plastic. (For method, please refer to DIN EN ISO 9227).

To demonstrate the constant distribution of the spray, at least two of the collecting recipients shall be placed at representative positions within the useable space. The target number is at least one recipient per 4 m2 of testing area.

When using the nozzle as described in Section 4.1, it has been proven appropriate to set  the flow-rate of the test solution sprayed over a defined period of time, with the help exclusively of the instrumentation and control equipment, provided. The specified test pressure and the suction height are to be maintained constant.

4.4 Compressed air

The compressed air with a pressure of approximately 70 to 180 kPa used to generate the salt spray may not exceed the limits for total oil content and percentage of solid contaminants as specified for class 1 cleanliness according to ISO 8573-1. The temperature of the water in the compressed air humidifier is to be set dependent on the pressure of the sprayed salt solution according DIN EN ISO 9227 (NSS-test).

5 Execution

5.1 Test conditions – Test procedure The test duration is to be stipulated upon on a case by case basis. The typical test duration is six full test cycles (6 weeks). If necessary, the test duration can be changed until it is possible to draw conclusions concerning the corrosion behaviour.

Interim assessments have proven useful to determine the progression of corrosion.

A full test cycle lasts 7 (Fig. 1) days and consists of:

3 times = 24h cycle A (Fig. 2; see also 7.2) without freezing phase, with 3 h salt spray phase (1 % NaCl solution)

3 times = 24h cycle B (Fig. 3; see also 7.2) without freezing phase, without salt spray, including assessment of specimens (or walk-around inspection)

1 time = 24h cycle C (Fig. 4; see also 7.2) with freezing phase, without salt spray

        Fig.1: The placement of specimens in the test chamber shall be carried out exclusively during the 
                 first cycle B of the evaluation phase. This also applies for the removal of the specimens.

                                 Fig.: 2: 24 h-cycle A, with 3 h salt spray phase (1 % NaCl)

        Fig.: 3: 24 h-cycle B without freezing phase, without salt spray, with evaluation phase

                                 Fig. 4: 24 h-cycle C, with freezing phase, without salt spray

5.2 Test interruption

Interruption of the test or opening of the test chamber is only permitted during the evaluation phase (cycle B). The test chamber may not be switched off during this time.

No interruption of the salt spray phase is permitted. Longer interruptions of the cyclic climate phases are to be avoided; if unavoidable, they must be mentioned in the test report.

5.3 Placing specimens in the chamber

The specimens shall preferably be positioned in the chamber at an angle of 65° to 75° relative to the horizontal with the side to be tested uppermost. Components are to be positioned as agreed with the principal, preferably in the orientation in which they will be installed. The specimens (or components) may not contact each other or shield other specimens from the salt spray.

When using two separate test chambers for the salt spray phase and the cyclic climate phase, the specimens may not be allowed to dry-out when being transferred from one chamber to the other.

Vehicle components or special corrosion test plates may also be used as specimens for the test. In the case of components, special care shall be taken to ensure that salt solution does not pool on the specimen, as this will affect the test conditions (climate). If this cannot be avoided, such pooling must be removed at least once a week.

6 Monitoring of the test system